Alloy K500
Nickel Based Alloy for Oil & Gas
HIGH STRENGTH - UFA
Certified Standards: |
Gems 100248736 |
ASTM B865 |
UNS N05500 |
W.St. 2.4375 |
SAE-AMS 4676 |
QQ-N-286 |
BS 3076-89 NA18 |
Nace MR01-75 / ISO15156 |
Nace MR01-03 |
PED 97/23/EC - 2014/68/EU |
Minimum mechanical properties to ASTM A370 |
Rp0.2% (yield) |
690MPa / 100KSI |
Rm (ultimate tensile) |
965MPa / 140KSI |
Elongation (A4) |
17% |
Reduction of Area |
25% Min |
Hardness (HRc) |
35 Max |
CHARPY IMPACT |
(-29°C - 1/4T - Longitudinal) |
Diameter 0.6" to 2.75" 27J Ave. / 20J Min.
|
(-29°C - 1/4T - Longitudinal) |
Diameter 2.8" to 12" 40.5J Ave. / 30J Min.
|
Alloy K500 Round Bar Size Range ex-stock |
Machined Round Bar - sawn to length if required |
Dia. Metric (mm) |
Dia. Imp. (inch) |
Tol. |
10.00 |
0.394 |
BG h9 |
15.88 |
0.625 |
Peeled h9 |
19.05 |
0.750 |
Peeled h9 |
25.40 |
1.000 |
Peeled K11 |
31.75 |
1.250 |
Peeled K11 |
38.10 |
1.500 |
Peeled K11 |
44.45 |
1.750 |
Peeled K11 |
50.80 |
2.000 |
Peeled K11 |
57.15 |
2.250 |
Peeled K11 |
63.50 |
2.500 |
Peeled K11 |
69.85 |
2.750 |
Peeled K11 |
76.20 |
3.000 |
Peeled K11 |
82.55 |
3.250 |
Peeled K11 |
88.90 |
3.500 |
Peeled K11 |
101.60 |
4.000 |
Peeled K12 |
114.30 |
4.500 |
Peeled K12 |
127.00 |
5.000 |
Peeled K12 |
139.70 |
5.500 |
Peeled K12 |
152.40 |
6.000 |
Peeled K12 |
165.10 |
6.500 |
Peeled K12 |
177.80 |
7.000 |
Peeled K12 |
190.50 |
7.500 |
Peeled K12 |
203.20 |
8.000 |
Peeled K12 |
215.90 |
8.500 |
Turned -0/+1mm |
228.60 |
9.000 |
Turned -0/+1mm |
254.00 |
10.000 |
Turned -0/+1mm |
279.40 |
11.000 |
Turned -0/+1mm |
304.80 |
12.000 |
Turned -0/+1mm |
View ISO Tolerances
Make an Enquiry